1. Nnwale nyocha na nyocha
Nke 3valvụ tayasamples nke ụlọ ọrụ nyere, 2 bụ valves, na 1 bụ valvụ nke na-ejibeghị. Maka A na B, valvụ a na-ejighị mee ihe bụ akara ntụ ntụ. Ihe osise zuru oke 1. Ihe dị n'elu nke valve A bụ nke na-emighị emi, elu nke valve B bụ elu, elu nke valve C bụ elu, na elu nke valve C bụ elu. A na-eji ngwaahịa corrosion kpuchie Valves A na B. A na-agbaji valvụ A na B na bends, akụkụ dị n'èzí nke eriri ahụ dị n'akụkụ valvụ ahụ, valvụ mgbanaka ọnụ B na-agbaji na njedebe, na akụ na-acha ọcha n'etiti ebe gbawara agbawa n'elu valvụ A bụ akara. . Site na nke dị n'elu, mgbawa na-adị n'ebe nile, mgbawa bụ ndị kasị ibu, na mgbawa dị n'ebe nile.
Akụkụ nkevalvụ tayaA na-ebipụ ihe nlele A, B na C site na mgbada, wee hụ morphology nke elu site na iji microscope eletrọn nke ZEISS-SUPRA55 na-enyocha, ma jiri EDS nyochaa ihe mejupụtara micro-mpaghara. Ọgụgụ 2 (a) na-egosi microstructure nke elu valve B. Enwere ike ịhụ na e nwere ọtụtụ ihe ndị na-acha ọcha na ndị na-egbuke egbuke n'elu (nke a na-egosipụta site na akụ na-acha ọcha na ọnụ ọgụgụ ahụ), na nyocha EDS nke ihe ndị na-acha ọcha nwere nnukwu ọdịnaya nke S. Ihe nyocha nke ume ike nke ihe ndị na-acha ọcha. ka egosiri na onyonyo 2(b).
Ọnụ ọgụgụ 2 (c) na (e) bụ microstructures elu nke valvụ B. Enwere ike ịhụ ya site na eserese 2 (c) na elu ahụ fọrọ nke nta ka ọ bụrụ ihe niile na-emepụta ihe na-emepụta ihe, na ihe ndị na-emebi emebi nke ngwaahịa corrosion site na nyocha ume ike. tumadi gụnyere S, Cl na O, ọdịnaya nke S na ọnọdụ onye ọ bụla dị elu, a na-egosipụtakwa nsonaazụ nyocha ume ume na Fig. 2 (d). Enwere ike ịhụ ya site na eserese 2 (e) na enwere micro-cracks tinyere mgbanaka valvụ n'elu valve A. Ọnụ ọgụgụ 2 (f) na (g) bụ micro-morphologies elu nke valve C, elu dịkwa elu. kpuchiri ya kpamkpam site na ngwaahịa corrosion, na ihe ndị na-emebi emebi na-agụnye S, Cl na O, dị ka Figure 2 (e). Ihe kpatara mgbawa nwere ike ịbụ nrụgide corrosion cracking (SCC) site na nyocha ngwaahịa corrosion na elu valve. Fig. 2 (h) bụkwa microstructure elu nke valvụ C. Enwere ike ịhụ na elu ahụ dị ọcha, na ihe mejupụtara kemịkalụ nke elu nke EDS nyochara yiri nke ọla kọpa alloy, na-egosi na valvụ ahụ dị. emebibeghị. Site n'ịtụle morphology microscopic na ihe mejupụtara kemịkalụ nke oghere valvụ atọ ahụ, a na-egosi na enwere mgbasa ozi na-emebi emebi dị ka S, O na Cl na gburugburu gburugburu.
A na-emepe oghere nke valvụ B site na ule na-ehulata, a chọpụtakwara na mgbawa ahụ adịghị abanye n'ofe akụkụ nke valvụ ahụ, gbawara n'akụkụ nke azụ azụ, ma ghara ịgbawa n'akụkụ na-abụghị nke azụ azụ. nke valvụ. Nleba anya nke mgbaji ahụ na-egosi na agba agbaji agbaji agbaji, na-egosi na agbaji agbaji agbajiwo, na akụkụ ụfọdụ nke mgbawa ahụ nwere agba gbara ọchịchịrị, nke na-egosi na mmebi ahụ dị njọ na akụkụ ndị a. Ahụrụ mgbawa nke valvụ B n'okpuru microscope eletrọn na-enyocha, dị ka egosiri na foto 3. Ihe osise 3 (a) na-egosi ọdịdị macroscopic nke valvụ B mgbawa. Enwere ike ịhụ na mgbaji dị n'èzí dị nso na valvụ ahụ ejirila ngwaahịa corrosion kpuchie ya, ọzọ na-egosi ọnụnọ nke mgbasa ozi na-emebi emebi na gburugburu ebe obibi. Dị ka ike ụdịdị ike nyocha, kemịkal nke ngwaahịa corrosion bụ tumadi S, Cl na O, na ọdịnaya nke S na O dịtụ elu, dị ka e gosiri na fig. 3(b). N'ileba anya n'elu mgbawa ahụ, a na-achọpụta na usoro nrịbawanye na-eto eto dị n'akụkụ ụdị kristal. A pụkwara ịhụ ọnụ ọgụgụ buru ibu nke mgbawa nke abụọ site n'ịhụ mgbawa na ọkwa dị elu, dị ka e gosiri na foto 3 (c). Akara mgbawa nke abụọ nwere akụ na-acha ọcha na ọnụ ọgụgụ ahụ. Ngwaahịa ndị na-emebi emebi na ụkpụrụ ntolite n'elu mgbawa ahụ na-egosikwa njirimara nke mgbawa corrosion nrụgide.
E mepebeghị mgbawa nke valvụ A, wepụ akụkụ nke valvụ (gụnyere ọnọdụ gbawara agbawa), gwerie ma kpochaa akụkụ axial nke valvụ ahụ, ma jiri Fe Cl3 (5 g) + HCl (50 mL) + C2H5OH ( 100 ml) ihe ngwọta ka edobere, wee hụ n'usoro metallographic na mgbape morphology site na Zeiss Axio Observer A1m anya microscope. Ihe osise 4 (a) na-egosi nhazi metallographic nke valvụ, nke bụ α + β dual-phase Ọdịdị, na β dị nnọọ mma na granular ma kesaa na α-phase matrix. E gosipụtara ụkpụrụ ịgbasa mgbawa na mgbawa okirikiri na eserese 4 (a), (b). Ebe ọ bụ na ihe mgbawa ahụ jupụtara na ngwaahịa corrosion, ọdịiche dị n'etiti oghere abụọ ahụ dị obosara, ọ na-esikwa ike ịmata ọdịiche nke usoro mgbasa. bifurcation onu. A na-ahụkwa ọtụtụ mgbawa nke abụọ (nke akụ na-acha ọcha akara na ọnụ ọgụgụ a) na mgbape isi a, lee Fig. 4(c), na mgbawa nke abụọ a gbasaa n'akụkụ ọka. A na-ahụ ihe nlele valvụ etched site na SEM, a chọpụtakwara na enwere ọtụtụ micro-cracks na ọnọdụ ndị ọzọ yiri mgbawa isi. Ihe ntanye ndị a sitere na elu ma gbasaa n'ime valvụ ahụ. Ihe mgbawa ahụ nwere nkewa wee gbasaa n'akụkụ ọka, lee eserese 4 (c), (d). The gburugburu ebe obibi na nchekasị ọnọdụ nke ndị a microcracks fọrọ nke nta ka ndị nke isi mgbape, n'ihi ya, ọ pụrụ inferred na isi mgbape si propagation ụdị bụkwa intergranular, nke na-kweere site mgbaji chọpụtara nke valvụ B. The bifurcation onu nke bifurcation onu. mgbawa ahụ na-egosikwa njirimara nrụgide corrosion cracking nke valvụ.
2. Nyocha na Mkparịta ụka
N'ịchịkọta, enwere ike ịpụta na mmebi nke valvụ ahụ na-akpata nrụgide corrosion cracking nke SO2 kpatara. Nchegbu corrosion cracking n'ozuzu kwesịrị izute ọnọdụ atọ: (1) ihe ndị na-emetụ n'ahụ corrosion nrụgide; (2) ihe na-emebi emebi na-enwe mmetụta maka ọla kọpa alloys; (3) ụfọdụ ọnọdụ nrụgide.
A na-ekwenyekarị na ọla ndị dị ọcha anaghị ata ahụhụ site na corrosion nrụgide, na alloys niile na-enwekwa ike imebi nrụgide ruo ogo dịgasị iche iche. Maka ihe ọla kọpa, a na-ekwenyekarị na nhazi nke akụkụ abụọ nwere nrụrụ aka corrosion dị elu karịa nhazi otu nkeji. A kọwapụtara na akwụkwọ akụkọ na mgbe ọdịnaya Zn dị na ihe ọla kọpa karịrị 20%, ọ na-enwe mmetụta nke corrosion nrụgide dị elu, na ọdịnaya Zn dị elu, nke na-eme ka ọ bụrụ ihe na-eme ka ọ dị elu. Ọdịdị metallographic nke nozzle gas na nke a bụ α + β dual-phase alloy, na ọdịnaya Zn dị ihe dị ka 35%, karịa 20%, ya mere ọ nwere mmetụta corrosion nrụgide dị elu ma na-ezute ọnọdụ ihe achọrọ maka nrụgide. corrosion cracking.
Maka ihe ọla kọpa, ọ bụrụ na emeghị nrụrụ aka mgbakasị ahụ mgbe arụrụ arụ ọrụ oyi gasịrị, nrụrụ nrụgide ga-eme n'okpuru ọnọdụ nrụgide kwesịrị ekwesị na gburugburu ebe na-emebi emebi. Nchegbu na-akpata nrụgide corrosion mgbawa bụ n'ozuzu nrụgide tensile nke mpaghara, nke enwere ike itinye nrụgide ma ọ bụ nrụgide fọdụrụnụ. Mgbe taya gwongworo ahụ gbasachara, a ga-ebute nrụgide nkwụ n'akụkụ axial direction nke ikuku ikuku n'ihi nnukwu nrụgide dị na taya ahụ, nke ga-eme ka mgbawa gburugburu na ikuku ikuku. Enwere ike ịgbakọ nrụgide tensile site na nrụgide ime taya dị ka σ = p R / 2t (ebe p bụ nrụgide dị n'ime nke taya ahụ, R bụ n'ime dayameta nke valvụ, na t bụ mgbidi mgbidi. valvụ). Otú ọ dị, n'ozuzu, nrụgide nrụgide na-akpata site na nrụgide dị n'ime nke taya adịghị oke ibu, na mmetụta nke nrụgide fọdụrụnụ kwesịrị ịtụle. Ọnọdụ mgbawa nke gas nozzles niile dị na azụ azụ, ma o doro anya na nrụrụ ihe fọdụrụ na azụ azụ dị ukwuu, na enwere nrụgide nkwụsị nke fọdụrụ n'ebe ahụ. N'ezie, n'ọtụtụ ihe ndị na-eme ọla kọpa na-arụ ọrụ nke ọma, nrụgide corrosion adịghị adịkarị n'ihi nrụgide imewe na-akpata, ọtụtụ n'ime ha na-akpatakwa nrụgide fọdụrụnụ nke a na-ahụghị ma na-eleghara anya. N'okwu a, na nkwụghachi azụ nke valvụ ahụ, ntụziaka nke nrụgide nrụgide na-emepụta site na nrụgide dị n'ime nke taya na-adabere na ntụziaka nke nrụgide fọdụrụnụ, na nchikota nke nrụgide abụọ a na-enye ọnọdụ nrụgide maka SCC. .
3. Mmechi na aro
Mmechi:
The cracking nkevalvụ tayaihe na-ebutekarị bụ nrụgide corrosion cracking nke SO2 kpatara.
Aro
(1) Chọpụta isi iyi nke ihe na-emebi emebi na gburugburu ebe obibi gburugburuvalvụ taya, ma gbalịa ka ị ghara ịkpakọrịta kpọmkwem na ihe na-emebi emebi gbara ya gburugburu. Dịka ọmụmaatụ, enwere ike itinye akwa mkpuchi mgbochi corrosion n'elu valvụ ahụ.
(2) Enwere ike iwepụ nrụgide nkwụsị nke fọdụrụ na-arụ ọrụ oyi site na usoro kwesịrị ekwesị, dị ka mgbakasị ahụ mgbakasị ahụ mgbe ọ gbasịrị.
Oge nzipu: Sep-23-2022